Sample | d = 8.955 Å [37] | d = 3.976 Å [37] | d = 2.973 Å [37] | IR, % | |||
---|---|---|---|---|---|---|---|
d | IN | d | IN | d | IN | ||
N-CLI | 8.959 | 622 | 3.963 | 705 | 2.970 | 335 | 100 |
0.25H-CLI | 8.951 | 999 | 3.960 | 444 | 2.970 | 220 | 100 |
0.5H-CLI | 8.936 | 999 | 3.961 | 481 | 2.973 | 229 | 103 |
1H-CLI | 8.939 | 999 | 3.960 | 538 | 2.970 | 260 | 108 |
3H-CLI | 8.953 | 608 | 3.958 | 553 | 2.971 | 240 | 84 |
Pd(II)–Cu(II)/0.25H-CLI | 8.941 | 999 | 3.961 | 524 | 2.972 | 262 | 107 |
Pd(II)–Cu(II)/0.5H-CLI | 8.953 | 945 | 3.962 | 543 | 2.974 | 262 | 102 |
Pd(II)–Cu(II)/1H-CLI | 8.945 | 999 | 3.959 | 479 | 2.973 | 218 | 94 |
Pd(II)–Cu(II)/3H-CLI | 8.968 | 378 | 3.964 | 285 | 2.978 | 122 | 56 |