Polymer | Mole ratio 3:4 | Average % yielda | Average E factora | Average 1H NMR Mn (Da)a | Standard deviationb | % RSDb | Polydispersity (PDI) |
---|---|---|---|---|---|---|---|
1a | 0.056 | 77 | 35 | 1.1 × 104 | 4.0 × 101 | 0.40 | 1.03 |
1b | 0.11 | 71 | 36 | 1.1 × 104 | 1.5 × 103 | 14 | 1.03 |
1c | 0.17 | 83 | 28 | 1.2 × 104 | 1.1 × 103 | 9.3 | 1.04 |
1d | 0.23 | 76 | 30 | 1.2 × 104 | 4.2 × 102 | 3.6 | 1.03 |
1e | 0.28 | 79 | 27 | 1.3 × 104 | 4.0 × 101 | 0.30 | 1.03 |
1f | 0.34 | 81 | 25 | 1.3 × 104 | 3.7 × 102 | 2.7 | 1.04 |
1g | 0.45 | 77 | 24 | 1.8 × 104 | 1.6 × 103 | 9.2 | 1.04 |
1h | 0.56 | 73 | 22 | 1.9 × 104 | 6.1 × 102 | 3.3 | 1.04 |
1i | 0.68 | 79 | 20 | 2.0 × 104 | 8.5 × 102 | 4.2 | 1.05 |
1j | 0.79 | 77 | 19 | 2.3 × 104 | 1.9 × 103 | 8.3 | 1.05 |
1k | 0.90 | 76 | 18 | 2.4 × 104 | 8.6 × 102 | 3.6 | 1.04 |
1l | 0.96 | 68 | 22 | 2.5 × 104 | 1.6 × 103 | 6.1 | 1.05 |
2 | 0.00 | N.D. | N.D. | 9.7 × 103 | 1.3 × 103 | 13 | 1.05 |