Synthesis, inhibition effects and quantum chemical studies of a novel coumarin derivative on the corrosion of mild steel in a hydrochloric acid solution

Abstract

Background

The acid corrosion inhibition process of mild steel in 1 M HCl by 4-[(2-amino-1, 3, 4-thiadiazol-5-yl)methoxy]coumarin (ATC), has been investigated using weight loss technique and scanning electron microscopy (SEM). ATC was synthesized, and its chemical structure was elucidated and confirmed using spectroscopic techniques (infrared and nuclear magnetic resonance spectroscopy).

Findings

The results indicated that inhibition efficiencies were enhanced with an increase in concentration of inhibitor and decreased with a rise in temperature. The adsorption equilibrium constant (K) and standard free energy of adsorption (ΔGads) were calculated. Quantum chemical parameters such as highest occupied molecular orbital energy, lowest unoccupied molecular orbital energy (EHOMO and ELUMO, respectively) and dipole moment (μ) were calculated and discussed. The results showed that the corrosion inhibition efficiency increased with an increase in both the EHOMO and μ values but with a decrease in the ELUMO value.

Conclusions

Our research show that the synthesized macromolecule represents an excellent inhibitor for materials in acidic solutions. The efficiency of this macromolecule had maximum inhibition efficiency up to 96 % at 0.5 mM and diminishes with a higher temperature degree, which is revealing of chemical adsorption. An inhibitor molecule were absorbed by metal surface and follow Langmuir isotherms low and establishes an efficient macromolecule inhibitor having excellent inhibitive properties due to entity of S (sulfur) atom, N (nitrogen) atom and O (oxygen) atom.

Background

It is very important to use corrosion inhibitors to prevent metal dissolution and minimize acid consumption [14]. The majority of well-known acid inhibitors are organic compounds that contain nitrogen, sulfur and oxygen atoms. The inhibitory action exercised by organic compounds on the dissolution of metallic species is normally related to adsorption interactions between the inhibitors and the metal surface. The planarity (p) and lone pairs of electrons present on N, O and S atoms are important structural features that control the adsorption of these molecules onto the surface of the metal [57]. The effective and efficient corrosion inhibitors are those compounds that have π-bonds, contain hetero-atoms such as sulfur, nitrogen, oxygen and phosphorous and allow the adsorption of compounds on the metal surface [811]. The organic inhibitors decrease the corrosion rate by adsorbing on the metal surface and blocking the active sites by displacing water molecules, leading to the formation of a compact barrier film on the metal surface. Coumarins exhibit pharmacological activities, such as anticancer, anti-inflammatory [12], anti-influenza, antituberculosis [13], anti-HIV, antiviral, antialzheimer and antimicrobial activities [14]. Nowadays researchers go for coumarins to used as corrosion inhibitors due to the electronic structure, planarity, lone pairs of electrons present on oxygen and stability [1517]. The successful control of corrosion develops the life of mechanical hardware. Nowadays corrosion inhibitors have more significant, due to their usage in industries. Organic inhibitors considered as eco-friendly much more than inorganic one. Organic inhibitors decreasing the corrosion rate by adsorbing onto the surface of the metal through the active sites namely phosphorus, sulfur, oxygen, nitrogen atoms or pi-bonds [18]. Recently the quantum chemical computations based on density function theory (DFT) become powerful investigation theoretical tool for researchers to investigate the ability of organic molecules as corrosion inhibitions. This tool offers a glance at physical insights on corrosion inhibition mechanisms [19]. In continuation of previous work [2027], we focus herein on the design our approach to increase the inhibitive properties based on conjugated system and electron density, in addition to applied the theoretical studies to associate the inhibitive properties with electronic structures. Initially we were starting from 4-hydroxycoumarin as starting material for the synthesis of 4-[(2-amino-1, 3, 4-thiadiazol-5-yl)methoxy]coumarin (ATC) contain 1, 3, 4-thiadiazol moiety.

Methods

Chemistry

The chemicals utilized were supplied by Sigma-Aldrich and the purity checked by TLC (thin layer chromatography). Infrared spectra were obtained on a Thermo Scientific, NICOLET 6700 FTIR spectrometer. Nuclear magnetic resonance spectra were obtained on a JEOL JNM-ECP 400. Elemental microanalysis, was carried out using a model 5500-Carlo Erba C.H.N elemental analyzer.

Synthesis of corrosion inhibitor “4-[(2-amino-1, 3, 4-thiadiazol-5-yl)methoxy]coumarin (ATC)”

This compound was synthesized in good yield according to the previously described procedures [28, 29]. Phosphorus oxychloride (20 ml) was added to 2-(2-oxo-2H-chromen-4-yloxy) acetic acid (0.05 mol) and the mixture was stirred for I h at room temperature. Thiosemicarbazide (4.56 g, 0.05 mol) was added and the mixture was heated and reflux for 5 h. On cooling, the mixture was poured on to ice. After 4 h stir for 15 min to decompose the excess phosphorusoxychloride, then heated under reflux for 30 min, cooling, the mixture was neutralized by 5 % potassium hydroxide, the precipitated was filtered, washed with water, dried and crystallized. Recrystallization from dichloromethane yields 55 %, m.p. 99 °C; 1H-NMR (CDCl3): δ 5.62 (s, 1H, –C=C–H), δ 4.91 and δ 5.33 (d, 2H, t, 2H, for OCH2), δ 7.23–7.87 (m, 1H, C–H aromatic ring), δ5.21 (s, NH2); IR: 3314.5 and 3375.1 cm−1 (s, H, amine), 291.2 (C–H alkane); 3079.1 (C–H aromatic),1752.3 cm−1 (C=O, lactone), 1591.1 cm−1(C=N, imine), 1635.3 cm−1 (C=C aromatic); Anal. Calcd. for C12H9N3O3S: C 52.36 %, H 3.30 %, N 15.26 %. Experimentally: C 51.64 % H 2.92 % and N 14.94 %s.

Gravimetric information

Specimens

Mild steel specimens utilized throughout our work were supplied from “Metal-Samples-Company” (St. Marys, PA, United States). The weight composition percentages of the MS were: Iron, 99.21; Carbon, 0.21; Silicon, 0.38; Phosphorous, 0.09; S, 0.05; Manganese, 0.05; and Alaminuim, 0.01. The specimens were cleaned using the chemical cleaning procedures described in ASTM G1-03 test method [30]. All experiments were done in aerated and non stirred hydrochloric acid mediums contain various concentrations of (ATC).

Weight loss techniques

The MS specimens were suspended separately in duplicate in 200 mL of the test solution, with and without various concentrations (0.0, 0.05, 0.1, 0.15, 0.20, 0.25 and 0.50 mM) of the ATC. After 1, 2, 3, 4, 5, 10 and 24 h., of immersion time, at temperatures, namely, 303, 313, 323 and 333 K. The specimens were taken out, washed, dried, and weighed accurately. The inhibition efficiencies (% IE) values were calculated using of in Eq. 1.

$$ IE\left( \% \right) = \frac{{w_{o} - w_{1} }}{{w_{o} }} \times 100 $$
(1)

where, \( {\text{w}}_{\text{o}} \) is the weight loss value in the absence of ATC, and \( {\text{w}}_{1} \) is the weight loss values in the presence of ATC.

The corrosion rates (CR) were determined by using Eq. (2) [31, 32]

$$ C_{R} = \frac{87.6w}{at\rho } $$
(2)

Quantum chemical calculations

The molecular optimization was carried out using the density function theory (DFT)/B3LYP with basis set 6-31G. Quantum chemical calculations such as E HOMO (highest occupied molecular orbital energy), E LUMO (lowest unoccupied molecular orbital energy) and μ (dipole moment) were calculated and discussed.

Results and discussion

Weight loss method

Effect of concentration

Corrosion rate inhibition efficiencies were calculated for various concentrations of ATC for the duration 1, 2, 3, 4, 5, 10 and 24 h, at 303 K are shown in Figs. 1 and 2. ATC obviously diminutive the corrosion in acidic solutions for MS. The IE (%) raise with the increment of concentration of ATC and become the maximum at the highest concentration of ATC. The increment of inhibition efficiencies with the concentration imply the increase in the ATC as a potent of protection efficiency. This might be due to the adsorption of inhibitor molecule on the metal surface as a protective layer giving high inhibition efficiency. Moreover, ATC has different active sites due to N, O and S atoms that make complexation with the metal easy and that would increase its adsorption on the metal surface.

Fig. 1
figure 1

Influences of concentrations vs time for ATC on corrosion rate at 303 K

Fig. 2
figure 2

Influences of concentrations vs time for ATC on corrosion efficiencies at 303 K

Effect of temperature

A differentiation of the inhibition efficiencies of ATC on mild steel in acidic medium with and without of different concentrations of ATC at various temperatures (303, 313, 323 and 333 K) indicates that corrosion efficiency rise with increasing of concentration and reduced with temperature rise (Fig. 3). Generally when the organic compounds adsorbed, the heat of adsorption will be negative, and this mean the process was an exothermic, so this is why the inhibitor efficiencies reduces when the temperature rise.

Fig. 3
figure 3

Influences of concentrations vs temperatures for ATC on corrosion efficiencies at fixed time

Scanning electron microscopy, SEM

As shown in Fig. 4, metal surface, that was originally smooth and neat, crumbled from corrosion and turn into rough surface and was extremely damaged by acidic solution. From Fig. 5, the healed surface of the metal was not suffering from remarkable corrosion. The synthesized macromolecule that supply protection to the surface of the metal from the acid.

Fig. 4
figure 4

The SEM micrograph for MS in in acidic medium in absence of ATC

Fig. 5
figure 5

The SEM micrographs, for MS in acidic medium with 0.5 mM of the corrosion inhibitor at 30 °C for 5 h as immersion time in presence of ATC

Adsorption isotherm and mechanism of corrosion and inhibition

Generally, IE of corrosion inhibitors depend on the adsorption coefficient of MS. The stabilization of the adsorbed inhibitor molecules differ according to the type of adsorption is chemical or physical or both. Turn out it is needful to explore the interaction between the metal and the inhibitor through adsorption isotherms [33]. The action of corrosion inhibitor over MS surface can be interpreted according to adsorption isotherm. Generally adsorption be based on the morphology nature. The mechanism of adsorption of organic molecules on MS surface can be clarified by means of the investigation of adsorption isotherm and adsorptive conduct of the inhibitor. Langmuir, Frumkin, Temkin and Freundluich isotherms were the most considerably utilized adsorption isotherm [34]. The corrosion inhibitors of natural and synthetic organic inhibitors on MS in acidic medium can be showed by a molecular adsorption technique. The process of adsorption was impacted by the structures and nature of the molecules in addition to the nature of the surface/charged metals and the types of media used [35, 36]. Surface coverage (θ) for the various concentrations of the tested inhibitor was utilized to elucidate the preferable adsorption isotherm to determine the adsorption process. To estimated θ, it was proposed [37] that the inhibition efficiency is due fundamentally to the blocking effect of the adsorbed molecules or ions and so, Eq. (3) will be applied.

$$ {{\uptheta }} = \frac{{{\text{IE}}\% }}{100} $$
(3)

The plot of \( \frac{{{\text{C}}_{\text{inh}} }}{\theta } \) vs concentration of inhibitor (\( C_{inh} \)) produce a straight line with an approximately unit slope, indicating that the inhibitor under study obeys the Langmuir adsorption isotherm [38], as in the Eq. (4).

$$ \frac{{C_{\text{inh}} }}{\theta } = \frac{1}{{K_{ads} }} + C_{inh } $$
(4)

\( K_{ads} \) is the adsorption constant obtained from the intercept of the straight line.

Equation 5 give the association of the intercept of the straight line \( K_{ads} \) with the standard free energy \( \Updelta G_{ads}^{^\circ } \)

$$ \Updelta G_{ads}^{^\circ } = - RTln\left[ {55.5K_{ads} } \right] $$
(5)

whereas R is the universal gas constant, the number 55.5 is the molar concentration of water in solution and T is the absolute temperature.

From Fig. 6 we can calculate \( K_{ads} \) and \( \Updelta G_{ads}^{^\circ } \). \( \Updelta G_{ads}^{^\circ } \).

Fig. 6
figure 6

Linear equation

From Fig. 6 \( \Updelta G_{ads}^{^\circ } \) was calculated and it was −31.51 kJ/mol. The negatively charge for \( \Updelta G_{ads}^{^\circ } \)elucidate the natural adsorption of the ATC on the MS surface and the vigorous interaction through the ATC and MS surface. Generally, if \( \Updelta G_{ads}^{^\circ } \) is nearly −20 kJ/mol then it appropriate with physical adsorption, while if \( \Updelta G_{ads}^{^\circ } \) nearly −40 kJ/mol then it is chemical adsorption occurring with the sharing of electrons from molecules of the inhibitor to the MS surface. In our work the \( \Updelta G_{ads}^{^\circ } \) is around −40 kJ/mol and demonstrate mechanism of adsorption of ATC by means of chemical adsorption [39]. In hydrochloric acid solution the following mechanism is proposed for the corrosion of mild steel [40]. The anodic dissolution mechanism of mild steel is

$$ {\text{Fe}} + {\text{Cl}}^{ - } \leftrightarrow ({\text{FeCl}}^{ - } )_{\text{ads}} $$
$$ ({\text{FeCl}}^{ - } )_{\text{ads}} \leftrightarrow ({\text{FeCl}}^{ + } )_{\text{ads}} + {\text{e}}^{ - } $$
$$ ({\text{FeCl}}^{ + } )_{\text{ads}} \leftrightarrow {\text{Fe}}^{ + + } + {\text{Cl}}^{ - } $$

The cathodic hydrogen evolution mechanism is

$$ {\text{Fe}} + {\text{H}}^{ + } \leftrightarrow ({\text{FeH}}^{ + } )_{\text{ads}} $$
$$ ({\text{FeH}}^{ + } )_{{{\text{ads}}}} + {\text{e}}^{ - } ({\text{FeH}})_{{{\text{ads}}}} $$
$$ ({\text{FeH}}^{ + } )_{{{\text{ads}}}} + {\text{H}}^{ + } + {\text{e}}^{ - } \to {\text{Fe}} + {\text{H}}_{2} $$

Generally, the corrosion inhibition mechanism in an acid medium is adsorption of the inhibitor on the metal surface. The process of adsorption is influenced by different factors like the nature and charge of the metal, the chemical structure of the organic inhibitor and the type of aggressive electrolyte [4143].

Suggested mechanisms of actions of coumarin as inhibitor

Chemically the inhibitor is adsorbed on the metal surface and forms a protective thin film or chemical bonds form by reaction between the inhibitor and metal. The adsorption mechanism of organic inhibitors can proceed via one of these routes. 1st, charged molecules and metal attract electrostatically. 2nd, the interaction between unpaired electrons and the metal surface. 3rd, interaction between π-electrons and the metal surface. Organic inhibitors protect the metal surface by blocking cathodic or anodic reactions or both and forming insoluble complexes. The inhibition efficiency of our corrosion inhibitor against the corrosion of mild steel in 1 M hydrochloric acid can be explained according to the number of adsorption sites, charge density, molecular size, mode of interaction with the metal surface and ability of formation of metallic insoluble complex. The π electrons for the double bonds and free electrons on the oxygen and nitrogen atoms form chemical bonds with the metal surface as shown in Fig. 7.

Fig. 7
figure 7

The suggested mechanism of action of the ATC as corrosion inhibitor

Quantum chemical calculations

The structural nature of the organic corrosion inhibitor and inhibition mechanism can be described by density functional theory (DFT). This technique has been found to be successful in providing insights into the chemical reactivity and selectivity in terms of global parameters such as electro-negativity (v), hardness (g) and softness (S), and local softness (sđ~r Þ) [44, 45]. The design of the (ATC), for use as a corrosion inhibitor was based on several factors. First, the molecule contains oxygen, nitrogen and sulfur atoms as active centers. Second, (ATC), can be easily synthesized and characterized. Third, planarity and finaly the resonance structure of (ATC). Excellent corrosion inhibitors are usually organic compounds that not only offer electrons to unoccupied orbitals of the metal but also accept free electrons from the metal [46]. Quantum chemical theoretically calculations were used to investigated the interactions between metal and inhibitor [47]. Highest occupied molecular orbital (HOMO), lowest unoccupied molecular orbital (LUMO), and Fukui functions as well as the total electron density of (ATC), are presented in Fig. 7. The blue and red iso-surfaces depict the electron density difference; the blue regions show electron accumulation while the red regions show electron loss. Quantum parameters such as EHOMO, EHOMO and dipole moment are provided in Table 1. The HOMO regions for the molecule, which are the sites at which electrophiles attack and represent the active centers with the utmost ability to interact with the metal surface atoms, has contributions from carbonyl, methanimine and amine. On the other hand, the LUMO orbital can accept electrons from the metal using anti-bonding orbitals to form feedback bonds are saturated around the coumarin ring [48]. Correspondingly, a high value of the HOMO energy (EHOMO) indicates the tendency of a molecule to donate electrons to an appropriate acceptor molecule with low energy or an empty electron orbital, whereas the energy of the LUMO characterizes the susceptibility of molecule toward nucleophilic attack [49]. Low values of the energy of the gap ΔE = ELUMO−EHOMO implies that the energy to remove an electron from the last occupied orbital will be minimized, corresponding to improved inhibition efficiencies [50]. EHOMO value (Table 1) do not vary very significantly for (ATC), which means that any observed differences in the adsorption strengths would result from molecular size parameters rather than electronic structure parameters. The seemingly high value of ΔE is in accordance with the nonspecific nature of the interactions of the molecule with the metal surface. A relationship between the corrosion inhibition efficiency of the (ATC), with the orbital energies of the HOMO (EHOMO) and LUMO (ELUMO) as well as the dipole moment (μ) is shown in Table 1. As is clearly observed, the inhibition efficiency increases with an increase in EHOMO values along with a decrease in ELUMO values. The increasing values of EHOMO indicate a higher tendency for the donation of electrons to the molecule with an unoccupied orbital. Increasing values of EHOMO thus facilitate the adsorption of the inhibitor. Thus, enhancing the transport process through the adsorbed layer would improve the inhibition effectiveness of the inhibitor. This finding can be explained as follows. ELUMO indicates the ability of the molecule to accept electrons; therefore, a lower value of ELUMO more clearly indicates that the molecule would accept electrons [51]. The direction of a corrosion inhibition process can be predicted according to the dipole moment (μ). Dipole moment is the measure of polarity in a bond and is related to the distribution of electrons in a molecule. In spite of the fact that literature is conflicting on the utilization of μ as an indicator of the direction of a corrosion inhibition reaction, it is for the most part concurred that the adsorption of polar compounds having high dipole moments on the metal surface ought to prompt better inhibition efficiency. The data obtained from the present study indicate that the (ATC), inhibitor has the value of μ = 4.959 and highest inhibition efficiency (96.0 %). The dipole moment is another indicator of the electronic distribution within a molecule. A few researchers express that the inhibition efficiency increments with increasing values of the dipole moment, which relies on upon the sort and nature of molecules considered. However, there is a lack of agreement in the literature on the correlation between μ and IE  %, as in some cases no significant relationship between these values has been identified [52, 53]. The electron density (charge distribution) is saturated all around molecule; hence we should expect flat-lying adsorption orientations [48]. The local reactivity of molecule was analyzed by means of the Fukui indices (FI) to assess reactive regions in terms of nucleophilic (f+) and electrophilic (f−) behavior. Figure 8d shows that the f− functions of molecule correspond with the HOMO locations, indicating the sites through which the molecule could be adsorbed on the metal surface, whereas f+ (Fig. 8e) correspond with the LUMO locations, showing sites through which the molecule could interact with the nonbonding electrons in the metal. High f− values are associated with the nitrogen atoms of thiadiazole ring and oxygen of the pyrone ring, in addition to oxygen atom of the bridge.

Table 1 Calculated quantum chemical properties for the most stable conformation of (ATC)
Fig. 8
figure 8

Electronic properties of (a) 3d-structure of ATC; (b) HOMO orbital; (c) LUMO orbital; (d) total electron density; (e) Fukui (f−) function; f Fukui (f+) function

Mulliken charge

The Mulliken charge distribution of (ATC) is presented in Table 2. Atom can be easily donating its electron to the empty orbital of the metal if the Mulliken charges of the adsorbed center become more negative [54]. It could be readily observed that nitrogen, oxygen, sulfur and some carbon atoms have high charge densities. The regions of highest electron density are generally the sites to which electrophiles can attach [54, 55]. Therefore, N, O, S and some C atoms are the active centers, which have the strongest ability to bond to the metal surface. Conversely, some carbon atoms carry positive charges, which are often sites where nucleophiles can attach. Therefore, (ATC) can also accept electrons from Fe through these atoms. It has been reported that excellent corrosion inhibitors can not only offer electrons to unoccupied orbitals of the metal but also accept free electrons from the metal [56]. According to the description of frontier orbital theory, HOMO (Fig. 9) is often associated with the electron donating ability of an inhibitor molecule. The molecules have tendency to donate electrons to a metal with empty molecule orbital if they have high EHOMO values. ELUMO, conversely, indicates the ability of the molecule to accept electrons [57]. Acceptance of electrons from a metal surface is easier when the molecule has lower value of ELUMO. The gap between the LUMO and HOMO energy levels of inhibitor molecules is another important parameter. Low absolute values of the energy band gap (E = ELUMO−EHOMO) mean good inhibition efficiency [58].

Table 2 Charges (Mulliken charges) for the ATC
Fig. 9
figure 9

The three dimensional structure of ATC

Conclusions

Our research demonstrate that the synthesized macromolecule represents an excellent inhibitor for materials in acidic solutions. The efficiency of this macromolecule had maximum inhibition efficiency up to 96 % at 0.5 mM and diminish with a higher temperature degree, which is revealing of chemical adsorption. Inhibitor molecules were absorbed by metal surface and follow Langmuir isotherms low and establishes an efficient macromolecule inhibitor hading excellent inhibitive properties due to entity of S (sulfur) atom, N (nitrogen) atom and O (oxygen) atom. SEM (Scanning electron microscope) measurements were confirming the figuration of a protective metal surface. Inhibition study of synthesized macromolecules obviously expose their function in the protection of MS in 1 M HCl.

References

  1. Al-Amiery A, Binti Kassim F, Kadhum V, Mohamad A (2016) Synthesis and characterization of a novel eco-friendly corrosion inhibition for mild steel in 1 M hydrochloric acid. Sci Rep 6:19890. doi: 10.1038/srep19890

  2. Sing DN, Dey AK (1993) Synergistic effects of inorganic and organic cations on inhibitive performance of propargyl alcohol on steel dissolution in boiling hydrochloric acid solution. Corrosion 49:594–600

    Article  Google Scholar 

  3. Al-Amiery AA, Kadhum AAH, Mohamad AB, Musa AY, Li CJ (2013) Electrochemical study on newly synthesized chlorocurcumin as an inhibitor for mild steel corrosion in hydrochloric acid. Materials 6:5466–5477

    Article  CAS  Google Scholar 

  4. Arab ST, Noor EA (1993) Inhibition of acid corrosion of steel by some S-Alkylisothiouronium. Corrosion 49:122–129

    Article  CAS  Google Scholar 

  5. Khaled FH (2003) Investigation of the inhibitive effect of ortho-substituted on corrosion of iron in 0.5 M H2SO4 solutions. Mater Chem Phys 82:949–960

    Article  CAS  Google Scholar 

  6. Lin W (2001) Inhibiting effect of 2-mercaptopyrimidine on the corrosion of a low carbon steel in phosphoric acid. Corros Sci 43:1637–1644

    Article  Google Scholar 

  7. Shorky H, Yuasa M, Sekine I, Issa RM, El-Baradie HY, Gomma GK (1998) Corrosion inhibition of mild steel by schiff base compounds in various aqueous solutions. Corros Sci 40:2173–2186

    Article  Google Scholar 

  8. Cang H, Shi WY, Shao JL, Xu Q (2012) Synthesis and some physical properties of magnetite (Fe3O4) nanoparticles. Int J Electrochem Sci 7:5626

    CAS  Google Scholar 

  9. Ma H, Song T, Sun H, Li X (1020) Consecutively alternating adsorption of anionic and cationic polyelectrolytes on charged surfaces. Thin Solid Films 2008:516

    Google Scholar 

  10. El Ashry EH, El Nemr AS, Essawy A, Ragab S (2008) Problems and progress in organic coatings science and technology. Prog Org Coat 61:11

    Article  Google Scholar 

  11. Ju H, Kai ZP, Li Y (2008) Corrosion behaviour of magnesium/aluminium alloys in 3.5 wt.% NaCl. Corros Sci 50:865

    Article  CAS  Google Scholar 

  12. Egan D, O’Kennedy R, Moran E, Cox D, Prosser E, Thornes RD (1990) The pharmacology, metabolism, analysis, and applications of coumarin and coumarin-related compounds. Drug Metab Rev 22:503–529

    Article  CAS  Google Scholar 

  13. Devji T, Reddy C, Woo C, Awale S, Kadota S, CorrioMoniz D (2011) Pancreatic Anticancer activity of a novel geranylgeranylated coumarin derivative. Bioorg Med Chem Lett 21:57705773

    Article  Google Scholar 

  14. Yeh J-Y, Coumar MS, Horng J-T, Shiao H-Y, Lee H-L (2010) anti-influenza drug discovery: structure-activity relationship and mechanistic insight into novel angelicin derivatives. J Med Chem 53:1519–1533

    Article  CAS  Google Scholar 

  15. Al-Amiery AK, Mohamad A, How C, Junaedi S (2014) Inhibition of mild steel corrosion in sulfuric acid solution by new Schiff base. Materials 7(2):787–804

    Article  Google Scholar 

  16. Mohamad AB, Kadhum AAH, Al-Amiery AA, Ying LC, Musa AY (2014) Synergistic of a coumarin derivative with potassium iodide on the corrosion inhibition of aluminum alloy in 1.0 M H2SO4. Met Mater Int 20(3):459–467. doi:10.1007/s12540-014-3008-3

    Article  CAS  Google Scholar 

  17. Kadhum AAH, Mohamad AB, Hammed LA, Al-Amiery AA, San NH, Musa AY (2014) Inhibition of mild steel corrosion in hydrochloric acid solution by new coumarin. Materials 7(6): 4335–4348. doi:10.3390/ma7064335

  18. Banerjee G, Malhotra SN (1992) Contribution to adsorption of aromaticamines on mild-steel surface from HCl solutions by impedance, UV, and raman-spectroscopy. Corrosion 48:10

    Article  CAS  Google Scholar 

  19. Gece G (2008) The use of quantum chemical methods in corrosion inhibitor studies. Corros Sci 50:2981

    Article  CAS  Google Scholar 

  20. Al-Amiery AA, Al-Bayati R, Saour K, Radi M (2012) Cytotoxicity, antioxidant and antimicrobial activities of novel 2-quinolone derivatives derived from coumarins. Res Chem Intermed 38(358):559–569

    Article  CAS  Google Scholar 

  21. Al-Amiery A.A, Al-MajedyKadhum A.A.H, Mohamad A (2015) Novel macromolecules derived from coumarin: synthesis and antioxidant activity. Sci Rep 5: 11825. doi:10.1038/srep11825)

  22. Al-Amiery AA, Musa AY, Kadhum AAH, Mohamad A (2011) The antioxidant activity of new coumarin derivatives. Int J Mol Sci 12:5757–5761

    Google Scholar 

  23. Al-Amiery A, Kadhum A, Alobaidy A, Mohamad A, Hoon P (2014) Novel corrosion inhibitor for mild steel in HCl. Materials 7(2):662–672

    Article  CAS  Google Scholar 

  24. Al-Amiery AA, Kadhum AAH, Mohamad A (2012) Antifungal and antioxidant activities of pyrrolidonethiosemicarbazone complexes. Bioinorg Chem Appl 2012:1–5

    Article  Google Scholar 

  25. Al-Amiery AA (2012) Synthesis and antioxidant, antimicrobial evaluation, DFT studies of novel metal complexes derivate from Schiff base. Res Chem Intermed 38:745–759

    Article  CAS  Google Scholar 

  26. Obayes H, Alwan G, Alobaidy A, Al-Amiery A, Kadhum A, Mohamad A (2014) Quantum chemical assessment of benzimidazole derivatives as corrosion inhibitors. Chem Cent J 8:21

    Article  Google Scholar 

  27. Al-Amiery AA, Kadhum AAH, Mohamad A (2012) Antifungal activities of new coumarins. Molecules 17:5713–5723

    Article  CAS  Google Scholar 

  28. Al-Majedy Y, Kadhum K, Al-Amiery AAH (1982) A synthesis and characterization of some new 4-Hydroxy-coumarin derivatives. Molecules 19(8):11791–11799

    Article  Google Scholar 

  29. Kadhum AA, Al-Amiery AA, Shikara M, Kadhum AA, Al-Bayati R (1980) Synthesis, structure elucidation and DFT studies of new thiadiazoles. Int J Phys Sci 6:6692–6697

    Google Scholar 

  30. Junaedi S, Kadhum AAH, Al-Amiery AA, Mohamad AB, Takriff MS (2012) Synthesis and characterization of novel corrosion inhibitor derived from oleic acid: 2-Amino 5-Oleyl-1,3,4Thiadiazol (AOT). Int J Electrochem Sci 7:3543–3554

    CAS  Google Scholar 

  31. Deng Q, Shi HW, Ding NN, Chen BQ, He XP, Liu G, Tang Y, Long YT, Chen GR (2012) Novel triazolylbis-amino acidderivatives readily synthesized via click chemistry as potentialcorrosion inhibitors for mild steel in HCl. Corros Sci 57:220–227

    Article  CAS  Google Scholar 

  32. Tao Z, Hea W, Wang S, Zhang S, Zhou G (2012) A study of differential polarization curves and thermodynamic properties for mild steel in acidic solution with nitrophenyltriazole derivative. Corros Sci 60:205–213

    Article  CAS  Google Scholar 

  33. Ji Gopal, Dwivedi P, Sundaram S, Prakash R (2013) Inhibitive effect of chlorophytum borivilianum root extract on mild steel corrosion in HCl and H2SO4 solutions. Ind Eng Chem Res 52(10673):10681

    Google Scholar 

  34. Gopal J, Shukla SK, Dwived P, Sundaram S, Prakash R (2011) Inhibitive effect of argemone mexicana plant extract on acid corrosion of mild steel. Ind Eng Chem Res 50:11954–11959

    Article  Google Scholar 

  35. Zhang QB, Hua YX (2009) Corrosion inhibition of mild steel by alkylimidazolium ionic liquids in hydrochloric acid. Electrochim Acta 54:1881–1887

    Article  CAS  Google Scholar 

  36. Khaled KF (2010) Understanding corrosion inhibition of mild steel in acid medium by some furan derivatives: a comprehensive overview. J Electrochem Soc 157:C116–C124

    Article  CAS  Google Scholar 

  37. Aytac AU, Ozmen M, Kabasakaloğlu M (2005) Investigation of some Schiff bases as acidic corrosion of alloy AA3102. Mater Chem Phys 89:176–181

    Article  CAS  Google Scholar 

  38. Dandia A, Gupta L, Singh P, Quraishi MA (2013) Ultrasound-assisted synthesis of pyrazolo[3,4b]pyridines as potential corrosion inhibitors for mild steel in 1.0 M HCl. ACS Sustain. Chem Eng 1:1303–1310

    CAS  Google Scholar 

  39. Al-Amiery AA, Al-Majedy YK, Kadhum AAH, Mohamad AB (2015) New coumarin derivative as an eco-friendly inhibitor of corrosion of mild steel in acid medium molecules. Molecules 20:366–383

    Article  CAS  Google Scholar 

  40. Bavarian B, Kim Yeob, Reiner L (2003) Corrosion protection of steel rebar in concrete by migrating corrosion inhibitors, CORROSION 2003. Appl Electrochem 34:95

    Google Scholar 

  41. Al-Amiery AA, Kadhum AAH, Mohamad AB, Junaedi S (2013) A novel hydrazinecarbothioamide as a potential corrosion inhibitor for mild steel in HCl. Materials 6:1420–1430

    Article  CAS  Google Scholar 

  42. Rubaye A, Abdulwahid A, Al-Baghdadi S, Al-Amiery A, Kadhum A, Mohamad A (2015) Cheery sticks plant extract as a green corrosion inhibitor complemented with LC-EIS/MS Spectroscopy. Int J Electrochem Sci 10:8200–8209

    CAS  Google Scholar 

  43. Al-Amiery AA, Musa AY, Kadhum AAH, Mohamad A (2011) The use of umbelliferone in the synthesis of new heterocyclic compounds. Molecules 16:6833–6843

    Article  CAS  Google Scholar 

  44. Ebenso EE, Isabirye DA, Eddy NO (2010) Adsorption and quantum chemical studies on the inhibition potentials of some thiosemicarbazides for the corrosion of mild steel in acidic medium. Int J Mol Sci 11:2473–2498

    Article  CAS  Google Scholar 

  45. Ashassi-Sorkhabi H, Shaabani B, Seifzadeh D (2005) Effect of some pyrimidinic Schiff bases on the corrosion of mild steel in HCl solution. Electrochim Acta 50:3446–3452

    Article  CAS  Google Scholar 

  46. Khaleda KF, Fadl-Allahb SA, Hammoutic B (2009) Some benzotriazole derivatives as corrosion inhibitors for copper in acidic medium: experimental and quantum chemical molecular dynamics approach. Mater Chem Phys 117:148–155

    Article  Google Scholar 

  47. Bahrami MJ, Hosseini SMA, Pilvar P (2010) Experimental and theoretical investigation of organic compounds as inhibitors for mild steel corrosion in sulfuric acid medium. Corros Sci 52:2793–2803

    Article  CAS  Google Scholar 

  48. Cruz J, Pandiyan T, Garcıa-Ochoa E (2005) A new inhibitor for mild carbon steel: electrochemical and DFT studies. J Electroanal Chem 583:8–16

    Article  CAS  Google Scholar 

  49. Costa JM, Lluch JM (1984) The use of quantum mechanics calculations for the study of corrosion inhibitors. Corros Sci 24:924–933

    Article  Google Scholar 

  50. Khalil N (2003) Quantum chemical approach of corrosion inhibition. Electrochim Acta 48:2635–2640

    Article  CAS  Google Scholar 

  51. Al-Amiery AA (2012) Antimicrobial and antioxidant activities of new metal complexes derived from (E)-3-((5-phenyl-1,3,4-oxadiazol-2-ylimino)methyl)naphthalen-2-ol. Med Chem Res 21:3204–3213

    Article  CAS  Google Scholar 

  52. Xia S, Qiu M, Yu L, Liu F, Zhao H (2008) Molecular dynamics and density functional theory study on relationship between structure of imidazoline derivatives and inhibition performance. Corros Sci 50:2021–2029

    Article  CAS  Google Scholar 

  53. Musa AY, Kadhum AH, Mohamad AB, Rahoma AB, Mesmari H (2010) Electrochemical and quantum chemical calculations on 4,4-dimethyloxazolidine-2-thione as inhibitor for mild steel corrosion in hydrochloric acid. J Mol Struct 969:233–327

    Article  CAS  Google Scholar 

  54. Obot IB, Ebenso EE, Akpan IA, Gasem ZM, Alfobi Ayo S (2012) Thermodynamic and density functional theory investigation of sulphathiazole as green corrosion inhibitor at mild steel/hydrochloric acid interface. Int J Electrochem Sci 7:1978–1996

    CAS  Google Scholar 

  55. Obot IB, Obi-Egbedi NO (2011) Anti-corrosive properties of xanthone on mild steel corrosion in sulphuric acid: experimental and theoretical investigations. Curr Appl Phys 11:382–392

    Article  Google Scholar 

  56. Obot IB, Obi-Egbedi NO, Eseola AO (2011) Anticorrosion potential of 2-Mesityl-1H-imidazo[4,5-f][1,10]phenanthroline on mild steel in sulfuric acid solution: experimental and theoretical study. Ind Eng Chem Res 50:2098–2110

    Article  CAS  Google Scholar 

  57. Obot IB, Obi-Egbedi NO (2010) Theoretical study of benzimidazole and its derivatives and their potential activity as corrosion inhibitors. Corros Sci 52:657–660

    Article  CAS  Google Scholar 

Download references

Authors’ contributions

AAA the principle investigator and wrote the main manuscript text. KFA and SBA evaluated the corrosion inhibitor with surface characterization, AZM, SAM and TKA were synthesis the inhibitor and prepared Figures while ABM and AHK were co-investigators and prepared part of characterization. All authors read and approved the final manuscript.

Acknowledgements

The authors gratefully acknowledge the Universiti Kebangsaan Malaysia under Grant DIP-2012-02.

Competing interests

The authors declare that they have no competing interests.

Author information

Authors and Affiliations

Authors

Corresponding author

Correspondence to Ahmed A. Al-Amiery.

Rights and permissions

Open Access This article is distributed under the terms of the Creative Commons Attribution 4.0 International License (http://creativecommons.org/licenses/by/4.0/), which permits unrestricted use, distribution, and reproduction in any medium, provided you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The Creative Commons Public Domain Dedication waiver (http://creativecommons.org/publicdomain/zero/1.0/) applies to the data made available in this article, unless otherwise stated.

Reprints and permissions

About this article

Check for updates. Verify currency and authenticity via CrossMark

Cite this article

Al-Azawi, K.F., Al-Baghdadi, S.B., Mohamed, A.Z. et al. Synthesis, inhibition effects and quantum chemical studies of a novel coumarin derivative on the corrosion of mild steel in a hydrochloric acid solution. Chemistry Central Journal 10, 23 (2016). https://doi.org/10.1186/s13065-016-0170-3

Download citation

  • Received:

  • Accepted:

  • Published:

  • DOI: https://doi.org/10.1186/s13065-016-0170-3

Keywords