Table 1 EDX analysis on CuS hexagonal plates

From: Optimization of reaction parameters in hydrothermal synthesis: a strategy towards the formation of CuS hexagonal plates

Area/ Spot Cu Atomic % S Atomic %
Area 1A 51.53 48.47
Spot 1B 48.28 51.72
Spot 1C 51.40 48.60
Spot 1D 48.08 51.92
Spot 1E 49.11 50.89
Spot 1 F 50.55 49.45
Spot 1G 50.24 49.76
Average 49.88 50.12
  1. Synthesis was conducted at 155°C with Cu 2 + : S 2 O 3 2 mole ratio of 1: 2 for 12 hours with reference to Figure 3.