Facile synthesis of flower like copper oxide and their application to hydrogen peroxide and nitrite sensing
Chemistry Central Journal volume 5, Article number: 75 (2011)
The detection of hydrogen peroxide (H2O2) and nitrite ion () is of great important in various fields including clinic, food, pharmaceutical and environmental analyses. Compared with many methods that have been developed for the determination of them, the electrochemical detection method has attracted much attention. In recent years, with the development of nanotechnology, many kinds of micro/nano-scale materials have been used in the construction of electrochemical biosensors because of their unique and particular properties. Among these catalysts, copper oxide (CuO), as a well known p-type semiconductor, has gained increasing attention not only for its unique properties but also for its applications in many fields such as gas sensors, photocatalyst and electrochemistry sensors. Continuing our previous investigations on transition-metal oxide including cuprous oxide and α-Fe2O3 modified electrode, in the present paper we examine the electrochemical and electrocatalytical behavior of flower like copper oxide modified glass carbon electrodes (CuO/GCE).
Flower like copper oxide (CuO) composed of many nanoflake was synthesized by a simple hydrothermal reaction and characterized using field-emission scanning electron microscopy (FE-SEM) and X-ray diffraction (XRD). CuO modified glass carbon electrode (CuO/GCE) was fabricated and characterized electrochemically. A highly sensitive method for the rapid amperometric detection of hydrogen peroxide (H2O2) and nitrite () was reported.
Due to the large specific surface area and inner characteristic of the flower like CuO, the resulting electrode show excellent electrocatalytic reduction for H2O2 and oxidation of . Its sensitivity, low detection limit, fast response time and simplicity are satisfactory. Furthermore, this synthetic approach can also be applied for the synthesis of other inorganic oxides with improved performances and they can also be extended to construct other micro/nano-structured functional surfaces.
The detection of hydrogen peroxide (H2O2) is of great important in various fields including clinic, food, pharmaceutical and environmental analyses, because H2O2 is a chemical threat to the environment and the production of enzymatic reactions . Many methods have been developed for the determination of H2O2, such as titrimetry , spectrophotometry , chromatography  and chemiluminescence . Compared with the above detection methods, the electrochemical detection of H2O2 was introduced to achieve a low detection limit and a low cost compared with the other detection methods. In recent years, with the development of nanotechnology, many kinds of micro/nano-scale materials have been used in the construction of electrochemical biosensors because of their unique and particular properties. A number of excellent reports have focused on the electrochemical determination of H2O2 utilizing noble metals including gold , silver , platinum [8, 9], palladium , and graphene-Pt nanoparticle hybrid material , transition metals and their oxides or complexes, such as MnO2 , Mn-nitrilotriacetate acid nanowires , CuO nanoparticles , Cu-Ni(OH)2 , layered double hydroxide , prussian blue , conducting polymers  and nanocomposite MnO2/MWNTs, Ag/GO [19, 20], as well as enzyme and protein modified electrodes [21, 22]. The low detection limit achieved with such platforms especially metal nanoparticle based electrodes is due to the enhancement in the signal-to-noise (S/N) ratio and increased mass transport to the electrode surface [11, 21]. Although some chemically modified electrodes have been proposed to reduce the large overpotential required for the direct oxidation or reduction of H2O2, it is still interesting to develop new materials with high efficiency and small dimensions for the detection of H2O2.
Like H2O2, nitrite ion () is another often studied analyte in various fields including clinic, food, and environmental analyses because its excess level in the blood has been proved to lead to haemoglobin oxidation [23–26]. Also it may interact in the stomach with amines and amides forming highly carcinogenic N-nitrosamine, many of which are known to be carcinogens [27, 28]. Therefore, determination is important for environment security and public health. Although is electroactive at carbon electrodes, its oxidation requires undesirably high overpotential and the voltammetric determination of it suffers from interference from other compounds. In order to improve the selectivity of sensor, the operating potential should be efficiently lowered. Modified electrodes with suitable electro-catalysts on the surface of carbon electrodes can achieve the purpose with an improved oxidation response of [29–31].
Metal oxide electrodes possess some unique electrochemical properties compared to metal ones. Their advantages include enhancement of reaction rate due to redox couples of oxide species of two different states, as well as weak adsorption or complete exclusion of hydrogen species on an oxide surface . Among these catalysts, copper oxide (CuO), as a well known p-type semiconductor, has gained increasing attention not only for its unique properties but also for its applications in many fields such as gas sensors, photocatalyst and electrochemistry sensors [30, 32–36]. Continuing our previous investigations on transition-metal oxide including cuprous oxide and α-Fe2O3 [37, 38] modified electrode, in the present paper we examine the electrochemical and electrocatalytical behavior of flower like copper oxide modified glass carbon electrodes (CuO/GCE). CuO was characterized by Powder X-ray diffraction (XRD), Field emission scanning electron microscopes (SEM) and cyclic voltammetry (CV) measurements. The electrochemical properties of the modified electrode were evaluated with regards to electrocatalytical reduction of H2O2 and electrocatalytical oxidation of .
Reagents and apparatus
Cu(NO3)2·3H2O, NH3·H2O and hexamethylenetetramine was purchased from Shanghai Chemical Reagent Factory (Shanghai, China). NaNO2 and 30% H2O2 solution was purchased from Beijing Chemical Reagent Factory (Beijing, China). All of the other chemicals used were analytical grade and used without further purification. Double-distilled water was used for preparation of buffer and standard solutions. All solutions were purged with high-purity nitrogen for at least 30 min to remove oxygen. NaNO2 and H2O2 solution was diluted daily before the electrochemical measurements.
Electrochemical experiments were performed with CHI 440a electrochemical analyzer (ChenHua Instruments Co. Ltd., Shanghai, China) with a conventional three-electrode cell. The CuO/GCE, an Ag/AgCl and a platinum electrode was used as the working electrode, the reference and the auxiliary electrode, respectively.
Synthesis of flower like CuO
In a typical synthesis, 0.7345 g Cu(NO3)2·3H2O and 0.8230 g hexamethylenetetramine (HMT) were dissolved into 25 ml distilled water under magnetic stirring. After 5.0 ml NH3•H2O (5%) was introduced into the mixture under stirring, the clear solution was transferred into a Teflon-lined steel-stainless autoclave of 40 ml. The autoclave was allowed to cool down to room temperature naturally after the system had been hydrothermally treated at 160°C for 6 h. Black precipitates were collected, washed with distilled water and ethanol several times to remove impurities. Finally, the precipitates were dried in air at 50°C for 6 h.
Characterization of the samples
Powder X-ray diffraction (XRD) of the product was carried out on a Shimadzu XRD-6000 X-ray diffractometer equipped with Cu Kα radiation (λ = 0.154060 nm), employing a scanning rate of 0.02°s-1 and 2θ ranges from 20° to 70°. Field emission scanning electron microscopes (SEM) was obtained by JEOL JSM-6700 FESEM (operating at 10 kV).
The dispersed flower like CuO on the electrode were fabricated by the following way: Firstly, the glass carbon electrode (GCE, Φ = 3 mm) was polished with a 1700# diamond paper and washed successively with double distilled water and ethanol in an ultrasonic bath, then 15 cyclic scans were carried out in the potential of 2.0 to -2.0 V (vs. SCE) in the solution of 1.0 mol/l H2SO4. Secondly, 4 mg CuO was dispersed in 2 ml ethanol solution. Then 20 μl of CuO solution (2 mg/ml) was cast on the surface of GCE and dried in air. Thus flower like CuO modified GCE was obtained.
Results and discussion
Structures and morphology characterization
The morphology and micro-structure of the product were investigated by SEM. Figure 1(A) and 1(B, C) are the SEM images of the sample. The low-magnification SEM image reveals that a large number of flower like CuO (Figure 1A) formed, composed of many nanoflake with average thickness of about 40 nm (Figure 1B, C), which may bring a favorite electronic property. Figure 1(C) shows the typical XRD patterns of the as-synthesized products All diffractions can be indexed as monoclinic phased CuO by comparison with JCPDS card files No. 48-1548 (a = 4.62 Å, b = 3.43 Å, and c = 5.06 Å). No characteristic peaks of other impurities were detected.
Electrochemical property of flower like CuO modified GCE
Figure 2 shows the cyclic voltammetric responses of various electrodes in an oxygen-free 0.1 M phosphate buffer solution (PBS, pH 7.0). No redox peak was observed when the bare GCE was used as the work electrode (Figure 2a). While the CuO/GCE was employed as the work electrode, a pair of well-defined redox peaks was obtained (Figure 2b) with an average formal potential of -0.1895 V. The cathodic peak and anodic peak were -0.2820 V and -0.0970 V at a scan rate of 0.05 V/s, respectively. Obviously, the redox peaks were attributed to the electrochemical reaction of CuO. According to earlier reports , the cathodic peak corresponds to the reduction of CuO/Cu2O redox couple, and the anodic peak comes from the formation of CuO layer.
Electroreduction behavior and amperometric response of H2O2on the CuO/GCE
Figure 3(A) shows the cyclic voltammograms of the CuO/GCE in the absence and presence of H2O2. When H2O2 was added to the pH 7.0 PBS, compared with the system with no H2O2 present (a), an obvious increase of the reduction peak was observed in deoxygenized environment (b, c). However, no electrochemical reduction peak was observed when the cyclic voltammetric scan was performed at bare GCE under the same conditions (Inset in Figure 3). The experimental results indicated that the CuO/GCE exhibited excellent electrocatalytic activity to H2O2. Regarding the reduction peaks of H2O2 at CuO/GCE, the effect of potential scan rate was investigated clearly. As can been seen from Figure 3(B), the reduction peak current is proportional to the square root of scan rate in the range of 30-200 mV/s, ipa/μA = 3.193 + 1.431 v1/2/mV·s-1, R = 0.9998, indicating a diffusion controlled process .
The catalytic mechanism for the reduction of H2O2 can be assumed as Cu (II) was first electrochemically reduced to Cu (I), which reacted chemically with H2O2 and resulted in the conversion of H2O2 to H2O and in the regeneration of the catalyst .
Figure 4 illustrates current-time plots for the CuO/GCE with successive step changes of H2O2 concentration. As the H2O2 was injected into the stirring PBS, the steady-state currents reached another steady-state value (95% of the maximum) in less than 3 s. Such a fast response implies that the CuO can promote the oxidation of H2O2. The linear relationship between the catalytic current and the concentration is shown in the inset of the Figure 4. As can be seen, the CuO/GCE displays linear response range of 5.0 × 10-6 to 180.0 ×10-6 M (correlation coefficient: 0.9993), with a detection limit of 1.6 × 10-6 M at a signal-to-noise ratio of 3, which is comparable or lower than detection limits obtained with protein [22, 41] or Ag nanoparticle [42, 43] based electrochemical sensors. We have summarized various H2O2 sensors in Table 1 with respect to the linear range and the detection limit. It can be seen that the performance of the noble metal Pt nanoparticle based sensor [9, 11, 21] is excellent compared to the other material based electrode with respect to the linear range and the detection limit. Nevertheless, it should be noted that the detection limit achieved with the CuO/GCE sensor was comparable or lower than that of protein or Ag nanoparticle based electrodes [41–43], and further CuO was prepared by a simple hydrothermal reaction and didn't require diffusional redox mediator and enzyme loading.
Electrooxidation behavior and amperometric response of on the CuO/GCE
Figure 5(A) shows typical CVs of the CuO/GCE in the absence and presence of , at the scan rate of 0.05 V/s in the oxygen-free 0.1 M PBS (pH 7.0). A well-defined nitrite oxidation peak could be observed at ca. + 0.843 V vs. Ag/AgCl (Figure 5(A) b, c), which is corresponding to the convertion of to through a two-electron oxidation process . In contrast, no peak was observed when cyclic voltammogram of the same electrode was run in 0.1 M phosphate buffer solution (PBS) (Figure 5(A) a). Cyclic voltammogram of the bare GCE was also run in the 1 mM solution. The peak corresponding to the oxidation of nitrite appears at ca. +1.038 V vs. Ag/AgCl (Figure 5(A) inset d), 195 mV more positive potential than the one obtained for modified GCE, also being of smaller intensity. This result might be explained by CuO film providing abundant active sites improving the electrocatalytic activity for . The catalytic oxidation mechanism can be explained with the following process:
First, nitrite loses an electron to form NO2 [reaction (1)]. Second, this step is followed by a homogeneous disproportionation [reaction (2)] of NO2 into nitrate and nitrite, which can be written as the total reaction (3) [45, 46].
Regarding the oxidation peak of at CuO/GCE, the potential scan rate was investigated clearly as shown in Figure 5(B). The peak current is proportional to the square root of scan rate in the range of 10-200 mV/s, ipa/μA = -3.5542 - 1.9517 v1/2/mV·s-1, R = 0.9995, while the Epa shifted positively. The results suggested that the oxidation of was undergoing a diffusion controlled process .
Figure 6 illustrates current-time plots for the CuO/GCE under the optimized experimental conditions with successive step changes of concentration. As the was injected into the stirring PBS, the steady-state currents reached another steady-state value (95% of the maximum) in less than 3 s. Such a fast response implies that the CuO can promote the oxidation of . The linear relationship between the catalytic current and the concentration is shown in the inset of the Figure 6. As can be seen, the CuO/GCE displays linear response range of 1.0 × 10-6 to 91.5 ×10-6 M (correlation coefficient: 0.9994), with a detection limit of 3.6 ×10-7 M at a signal-to-noise ratio of 3 and a sensitivity of -25.53 μA/mM. Note that the obtained detection limit of 3.6 ×10-7 M is comparable or lower than those obtained with other electrochemical methods [30, 31, 47–50]. We have summarized various sensors in Table 2 with respect to the linear range and the detection limit. Compared with other reported values [30, 31, 47–50] in Table 2, CuO/GCE exhibits the comparable or lower detection limit but narrower linear range.
The potential interference for the detection of nitrite using this electrochemical sensor was also examined by adding the following ions into the PBS solution at the same concentration that was used for nitrite: K+, Na+, Mg2+, Zn2+, Cl-, and . None of the ions caused interference. The potential of nitrite oxidation is high and, as a result, other electroactive species present in complex like dopamine and ascorbic acid can in principle be oxidized as well, interfering with the nitrite analysis. However, the detection of nitrite was examined in presence of 20-fold amount of dopamine and ascorbic acid and showed no interference. This result is similar to that of the previous report , which demonstrates the selectivity of CuO based electrochemical sensor towards nitrite.
In summary, flower like CuO composed of many nanoflake with average thickness of 40 nm was synthesized by a simple hydrothermal reaction. Then a novel electrochemical sensor made of CuO onto GCE had been constructed. Due to the large specific surface area and inner characteristic of the flower like CuO, the resulting electrode show excellent electrocatalytic reduction for H2O2 and oxidation of . Its sensitivity, low detection limit, fast response time and simplicity are satisfactory. Furthermore, this synthetic approach can also be applied for the synthesis of other inorganic oxides with improved performances and they can also be extended to construct other micro/nano-structured functional surfaces.
Yao S, Xu J, Wang Y, Chen X, Xu Y, Hu S: A highly sensitive hydrogen peroxide amperometric sensor based on MnO2 nanoparticles and dihexadecyl hydrogen phosphate composite film. Anal. Chim. Acta. 2006, 557: 78-84. 10.1016/j.aca.2005.10.052.
Hurdis EC, Romeyn HJ: Accuracy of Determination of Hydrogen Peroxide by Cerate Oxidimetry. Anal Chem. 1954, 26 (2): 320-325. 10.1021/ac60086a016.
Lobnik A, Cajlakovic M: Sol-gel based optical sensor for continuous determination of dissolved hydrogen peroxide. Sens Actuators B: Chem. 2001, 74: 194-199. 10.1016/S0925-4005(00)00733-4.
Pinkernell U, Effkemann S, Karst U: Simultaneous HPLC determination of peroxyacetic acid and hydrogen peroxide. Anal Chem. 1997, 69: 3623-3627. 10.1021/ac9701750.
Rocha FRP, Torralba ER, Reis BF, Rubio AM, Guardia M: A portable and low cost equipment for flow injection chemiluminescence measurements. Talanta. 2005, 67: 673-677. 10.1016/j.talanta.2005.03.021.
Wang L, Wang E: A novel hydrogen peroxide sensor based on horseradish peroxidase immobilized on colloidal Au modified ITO electrode. Electrochem Commun. 2004, 67: 225-229.
Qin X, Wang H, Wang X, Miao Z, Fang Y, Chen Q, Shao X: Synthesis of dendritic silver nanostructures and their application in hydrogen peroxide electroreduction. Electrochim Acta. 2011, 56: 3170-3174. 10.1016/j.electacta.2011.01.058.
Polsky R, Gill R, Kaganovsky L, Willner I: Electrochemical Detection of Biomolecules. Anal Chem. 2006, 67: 2268-2271.
Chakraborty S, Raj CR: Pt nanoparticle-based highly sensitive platform for the enzyme-free amperometric sensing of H2O2. Biosen Bioelectron. 2009, 24: 3264-3268. 10.1016/j.bios.2009.04.015.
Huang J, Wang D, Hou H, You T: Electrospun Palladium Nanoparticle-Loaded Carbon Nanofibers and Their Electrocatalytic Activities towards Hydrogen Peroxide and NADH. Adv Funct Mater. 2008, 18: 441-448. 10.1002/adfm.200700729.
Dey RS, Raj CR: Development of an Amperometric Cholesterol Biosensor Based on Graphene-Pt Nanoparticle Hybrid Material. J Phys Chem C. 2010, 114: 21427-21433. 10.1021/jp105895a.
Lin YH, Cui XL, Li LY: Low-potential amperometric determination of hydrogen peroxide with a carbon paste electrode modified with nanostructured cryptomelane-type manganese oxides. Electrochem Commun. 2005, 7: 166-172. 10.1016/j.elecom.2004.12.005.
Liu S, Li L, Hao Q, Yin X, Zhang M, Li Q, Chen L, Wang T: A novel non-enzymatic hydrogen peroxide sensor based on Mn-nitrilotriacetate acid (Mn-NTA) nanowires. Talanta. 2010, 81: 727-731. 10.1016/j.talanta.2009.12.057.
Miao XM, Yuan R, Chai YQ, Shi YT, Yuan YY: Direct electrocatalytic reduction of hydrogen peroxide based on Nafion and copper oxide nanoparticles modified Pt electrode. J Electroanal Chem. 2008, 612: 157-163. 10.1016/j.jelechem.2007.09.026.
Gu A, Wang G, Gu J, Zhang X, Fang B: An unusual H2O2 electrochemical sensor based on Ni(OH)2 nanoplates grown on Cu substrate. Electrochim. Acta. 2010, 55: 7182-7187. 10.1016/j.electacta.2010.07.023.
Li MG, Chen SH, Ni F, Wang YL, Wang L: Layered double hydroxides functionalized with anionic surfactant: Direct electrochemistry and electrocatalysis of hemoglobin. Electrochim Acta. 2008, 53: 7255-7260. 10.1016/j.electacta.2008.03.033.
Ricci F, Amine A, Tuta CS, Ciucu AA, Lucarelli F, Palleschi G, Moscone D: Prussian Blue and enzyme bulk-modified screen-printed electrodes for hydrogen peroxide and glucose determination with improved storage and operational stability. Anal Chim Acta. 2003, 485: 111-120. 10.1016/S0003-2670(03)00403-3.
Lu Q, Zhou T, Hu SS: Direct electrochemistry of hemoglobin in PHEA and its catalysis to H2O2. Biosens Bioelectron. 2007, 22 (6): 899-904. 10.1016/j.bios.2006.03.015.
Xu B, Ye ML, Yu YX, Zhang WD: A highly sensitive hydrogen peroxide amperometric sensor based on MnO2-modified vertically aligned multiwalled carbon nanotubes. Analy Chim Acta. 2010, 674: 20-26. 10.1016/j.aca.2010.06.004.
Liu S, Tian J, Wang L, Sun X: A method for the production of reduced graphene oxide using benzylamine as a reducing and stabilizing agent and its subsequent decoration with Ag nanoparticles for enzymeless hydrogen peroxide detection. Carbon. 2011, 49: 3158-3164. 10.1016/j.carbon.2011.03.036.
Jena BK, Raj CR: Enzyme integrated silicate-Pt nanoparticle architecture: A versatile biosensing platform. Biosen Bioelectron. 2011, 67: 2960-2966.
Behera S, Raj CR: Mercaptoethylpyrazine promoted electrochemistry of redox protein and amperometric biosensing of uric acid. Biosen Bioelectron. 2007, 67: 556-561.
Huang YG, Ji JD, Hou QN: A study on carcinogenesis of endogenous nitrite and nitrosamine, and prevention of cancer. Mutat Res. 1996, 358: 7-14. 10.1016/0027-5107(96)00087-5.
Davis J, McKeegan KJ, Cardosi MF, Vaughan DH: Evaluation of phenolic assays for the detection of nitrite. Talanta. 1999, 50 (1): 103-112. 10.1016/S0039-9140(99)00110-1.
Davis J, Moorcroft MJ, Wilkins SJ, Compton RG, Cardosi MF: Electrochemical detection of nitrate and nitrite at a copper modified electrode. Analyst. 2000, 67: 737-742.
Moorcroft MJ, Davis J, Compton RG: Detection and determination of nitrate and nitrite: a review. Talanta. 2001, 54 (5): 785-803. 10.1016/S0039-9140(01)00323-X.
Lijinsky W, Epstein SS: Nitrosamines as environmental carcinogens. Nature. 1970, 225: 21-23. 10.1038/225021a0.
Wolf IA, Wasserman AE: Nitrates, nitrites, and nitrosamines. Science. 1972, 177: 15-19. 10.1126/science.177.4043.15.
Cao X, Wang N, Guo L: Facile synthesis of novel MnO2 hierarchical nanostructures and their application to nitrite sensing. Sens. Actuators B: Chem. 2009, 137: 710-714. 10.1016/j.snb.2008.11.023.
Šljukic B, Banks CE, Crossley An, Compton RG: Copper Oxide-Graphite Composite Electrodes: Application to Nitrite Sensing. Electroanalysis. 2007, 19 (1): 79-84. 10.1002/elan.200603708.
Langley CE, Šljukic B, Banks CE, Compton RG: Manganese Dioxide Graphite Composite Electrodes: Application to the Electroanalysis of Hydrogen Peroxide, Ascorbic Acid and Nitrite. Analytical Sciences. 2007, 67: 165-170.
Patil SA, Patil LA, Patil DR, Jain GH, Wagh MS: CuO-doped BSST thick film resistors for ppb level H2S gas sensing at room temperature. Sens Actuat B. 2007, 123 (1): 246-253. 10.1016/j.snb.2006.08.026.
Vastarellaa W, Nicastrib R: Enzyme/semiconductor nanoclusters combined systems for novel amperometric biosensors. Talanta. 2005, 66 (3): 627-633. 10.1016/j.talanta.2004.12.007.
Liu ZG, Zhou RX, Zheng XM: Comparative study of different methods of preparing CuO-CeO2 catalysts for preferential oxidation of CO in excess hydrogen. J Mol Catal A-Chem. 2007, 267 (1-2): 137-142. 10.1016/j.molcata.2006.11.036.
Luque GL, Rodriguez MC, Rivas GA: Glucose biosensors based on the immobilization of copper oxide and glucose oxidase within a carbon paste matrix. Talanta. 2005, 66 (2): 467-471. 10.1016/j.talanta.2004.07.019.
Li Y, Zhang Q, Li J: Direct electrochemistry of hemoglobin immobilized in CuO nanowire bundles. Talanta. 2010, 83 (1): 162-166. 10.1016/j.talanta.2010.08.056.
Zhang L, Li H, Ni YH, Li J, Liao KM, Zhao GC: Porous cuprous oxide microcubes for non-enzymatic amperometric hydrogen peroxide and glucose sensing. Electrochem Comm. 2009, 11: 812-815. 10.1016/j.elecom.2009.01.041.
Zhang L, Ni YH, Wang XH, Zhao GC: Direct electrocatalytic oxidation of nitric oxide and reduction of hydrogen peroxide based on α-Fe2O3 nanoparticles-chitosan composite. Talanta. 2010, 82: 196-201. 10.1016/j.talanta.2010.04.018.
Zen J, Chung H, Kumar AS: Flow injection analysis of hydrogen peroxide on copper-plated screen-printed carbon electrodes. Analyst. 2000, 125: 1633-1637. 10.1039/b004207m.
Engel D, Grabner EW: Copper Hexacyanoferrate-Modified Glassy Carbon: A Novel Type of Potassium-Selective Electrode. Ber Bunsenges Phys Chem. 1985, 89: 982-986.
Wang HY, Guan R, Fan CH, Zhu DX, Li GX: A hydrogen peroxide biosensor based on the bioelectrocatalysis of hemoglobin incorporated in a kieselgubr film. Sens Actuators B: Chem. 2002, 84: 214-218. 10.1016/S0925-4005(02)00027-8.
Zhao B, Liu Z, Liu G, Li Z, Wang J, Dong X: Silver microspheres for application as hydrogen peroxide sensor. Electrochem Commun. 2009, 11 (8): 1707-1710. 10.1016/j.elecom.2009.06.035.
Cui K, Song YH, Yao Y, Huang ZZ, Wang L: A novel hydrogen peroxide sensor based on Ag nanoparticles electrodeposited on DNA-networks modified glassy carbon electrode. Electrochem Commun. 2008, 10 (4): 663-667. 10.1016/j.elecom.2008.02.016.
Zhu NN, Xu Q, Li S, Gao H: Electrochemical determination of nitrite based on poly(amidoamine) dendrimer-modified carbon nanotubes for nitrite oxidation. Electrochem Commun. 2009, 11 (12): 2308-2311. 10.1016/j.elecom.2009.10.018.
Guidelli R, Pergola F, Raspi G: Voltammetric behavior of nitrite ion on platinum in neutral and weakly acidic media. Anal Chem. 1972, 44: 745-755. 10.1021/ac60312a018.
Yu C, Guo J, Gub H: Electrocatalytical Oxidation of Nitrite and Its Determination Based on Au@Fe3O4 Nanoparticles. Electroanalysis. 2010, 67: 1005-1011.
Wang P, Mai ZB, Dai Z, Li YX, Zou XY: Construction of Au nanoparticles on choline chloride modified glassy carbon electrode for sensitive detection of nitrite. Biosens Bioelectron. 2009, 24: 3242-3247. 10.1016/j.bios.2009.04.006.
Huang X, Li YX, Chen YL, Wang L: Electrochemical determination of nitrite and iodate by use of gold nanoparticles/poly(3-methylthiophene) composites coated glassy carbon electrode. Sens Actuators B. 2008, 67: 780-786.
Abbaspour A, Mehrgardi MA: Electrocatalytic activity of Ce(III)-EDTA complex toward the oxidation of nitrite ion. Talanta. 2005, 67 (3): 579-584. 10.1016/j.talanta.2005.03.036.
Casella IG, Gatta MM: Electrochemical reduction of and on a composite copper thallium electrode in alkaline solutions. J Electroanal Chem. 2004, 568: 183-188.
The authors thank the National Natural Science Foundation of China (21001004), Young Fund of Anhui Normal University (2008xqn61) for fund support. This work is also supported by the innovation lab platform of Anhui Normal University.
The authors declare that they have no competing interests.
LZ completed the electrochemical work, data treatment and drafted the manuscript. FY participated in data analysis. XZ carried out the work of preparation, participated in data collection. LY participated in data analysis. All authors have read and approved the final manuscript.
Authors’ original submitted files for images
Below are the links to the authors’ original submitted files for images.
Rights and permissions
Open Access This article is distributed under the terms of the Creative Commons Attribution 2.0 International License (https://creativecommons.org/licenses/by/2.0), which permits unrestricted use, distribution, and reproduction in any medium, provided the original work is properly cited.
About this article
Cite this article
Zhang, L., Yuan, F., Zhang, X. et al. Facile synthesis of flower like copper oxide and their application to hydrogen peroxide and nitrite sensing. Chemistry Central Journal 5, 75 (2011). https://doi.org/10.1186/1752-153X-5-75
- Phosphate Buffer Solution
- Copper Oxide
- Layered Double Hydroxide
- Prussian Blue
- Electrochemical Sensor